Formation of novel flower like silicon phases and evaluation of mechanical properties of hypereutectic melt spun Al 20Si 5Fe alloys with addition of V
Yazarlar (3)
Bülent Ecevit Üniversitesi, Türkiye
Kastamonu Üniversitesi, Türkiye
Prof. Dr. Fikret YILMAZ
Tokat Gaziosmanpaşa Üniversitesi, Türkiye
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale |
| Dergi Adı | Materials Science and Engineering A |
| Dergi ISSN | 0921-5093 Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q4 |
| Makale Dili | İngilizce |
| Basım Tarihi | 06-2014 |
| Cilt No | 607 |
| Sayı | 1 |
| Sayfalar | 368 / 375 |
| DOI Numarası | 10.1016/j.msea.2014.04.025 |
| Makale Linki | http://linkinghub.elsevier.com/retrieve/pii/S0921509314004705 |
| Özet |
| In this work, rapidly solidified hypereutectic Al-20Si-5Fe-. XV (X=0, 0.5 and 1) alloys were fabricated by melt spinning under vacuum. Microstructural and spectroscopic analyses were performed using SEM, TEM, TEM-MAPing, TEM-EDS and XRD measurements. Mechanical properties of the alloys were determined using DSI measurements. Experimental results indicated that addition of 0.5. wt% V to melt-spun Al-20Si-5Fe alloys induced formation of a novel flower-like Si phase. And addition of higher amount V (1. wt%), caused formation of refined Si phases and mostly hindered formation of Fe-bearing intermetallics. Observations along with manuscript strongly indicate that V modifies the Si phases by the impurity induced twinning (IIT). Changes in the dynamic microhardness of the samples were mainly determined by the size of Si phases. Addition of vanadium led to quite lower elastic modulus in the vanadium added alloys compared to base alloy. © 2014 Elsevier B.V. |
| Anahtar Kelimeler |
| Al-Si alloys | Fe-containing intermetallics | Melt spinning | Vanadium |
Science Direct
Formation of novel flower like silicon phases and evaluation of mechanical properties of hypereutectic melt spun Al 20Si 5Fe alloys with addition of V
BM Sürdürülebilir Kalkınma Amaçları
| Atıf Sayıları | |
| WoS | 15 |
| SCOPUS | 17 |
| Google Scholar | 19 |