Effect of Clinically Relevant Smear Layers and pH of Universal Adhesives on Dentin Bond Strength and Durability
Yazarlar (2)
Doç. Dr. Hüseyin HATIRLI Tokat Gaziosmanpaşa Üniversitesi, Türkiye
Doç. Dr. Kaan YERLİYURT Tokat Gaziosmanpaşa Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Journal of Adhesive Dentistry (Q1) | ||
| Dergi ISSN | 1461-5185 Dergi Bilgileri (2022) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 03-2022 |
| Cilt / Sayı / Sayfa | 24 / 1 / 87–94 | DOI | 10.3290/j.jad.b2838121 |
| Makale Linki | https://www.quintessence-publishing.com/deu/en/article-download/2838121/the-journal-of-adhesive-dentistry/2022/01/effect-of-clinically-relevant-smear-layers-and-ph-of-universal-adhesives-on-dentin-bond-strength-and-durability | ||
| UAK Araştırma Alanları |
Restoratif Diş Tedavisi
|
||
| Özet |
| Purpose To evaluate the effects of different smear layers on the microtensile bond strength (µTBS) of a reference two-step self-etch adhesive and two universal adhesives. Materials and Methods Mid-coronal dentin of 90 teeth was exposed and divided into three bur groups (coarse diamond, fine diamond, or tungsten carbide). Each bur-prepared group was further divided into three adhesive groups: Clearfil SE Bond (SE, Kuraray Noritake), Single Bond Universal (SB; 3M Oral Care), and G-Premio Bond (GP, GC). After adhesive application, 4-mm-thick resin composites were built up. Half of the teeth in each bur-adhesive group were used in immediate µTBS testing, and the others were tested after thermal aging (n = 5). Rectangular sticks were prepared using a low-speed diamond saw. For each tooth, 6 central sticks were used in the µTBS test. Statistical analysis was performed using three-way ANOVA and … |
| Anahtar Kelimeler |
| Bond strength | Microtensile bond strength | Self-etch adhesives | Smear layer | Universal adhesive |