effect of filler ratio in adhesive systems on shear bond strength of composite resin to porcelains
Yazarlar (4)
Ondokuz Mayis Üniversitesi, Türkiye
Prof. Dr. Işıl SARIKAYA
Ondokuz Mayis Üniversitesi, Türkiye
Ondokuz Mayis Üniversitesi, Türkiye
Ondokuz Mayis Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
|
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale |
| Dergi Adı | Operative Dentistry |
| Dergi ISSN | 0361-7734 Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SCI |
| Dergi Grubu | Q4 |
| Makale Dili | İngilizce |
| Basım Tarihi | 06-2009 |
| Cilt No | 34 |
| Sayı | 3 |
| Sayfalar | 299 / 305 |
| DOI Numarası | 10.2341/08-88 |
| Özet |
| This in vitro study evaluated the effect of six different adhesive systems on the shear bond strength of resin composite to feldspathic and low-fusing porcelains. Sixty porcelain blocks were prepared for each low-fusing (Matchmaker) and feldspathic (MVK95) porcelain specimen. After surface preparation, the porcelain specimens were divided into six groups (n=10) for different adhesive systems (Adper Prompt L-Pop, QuadrantUnil Bond, Te-Econom, PQ1, One-StepPlus and Prime&Bond NT). After adhesive application, a universal resin composite (FiltekZ250) was condensed on the specimens. The prepared specimens were then stored in distilled water at 37°C for 24 hours, then all the samples were thermal cycled 1000 times between 5°C and 55°C. Shear testing was performed on a universal test machine using a crosshead speed of 0.5 mm/minute. The statistical analysis of the bond strength data included two-way ANOVA. Then, the means were compared by Tukey HSD test (aα=0.05). The lowest bond strength was observed in Adper Prompt L-Pop. No statistically significant difference was observed between One-Step Plus and Prime&Bond NT. The highest bond strength was observed in PQ1. When low- fusing or feldspathic porcelain restorations are repaired with resin composite, self-etching adhesive systems may not be indicated. If maximum bond strength is the goal in porcelain resin bonding, adhesive systems that have a high filler ratio should be used. |