Effects of boronizing on the microhardness and wear behaviour of AISI 1050 steel and chilled cast iron
Yazarlar (4)
Süleyman Demirel Üniversitesi, Türkiye
Dr. Öğr. Üyesi Mithat ŞİMŞEK
Gaziosmanpaşa Üniversitesi, Türkiye
Çankaya Üniversitesi, Türkiye
Süleyman Demirel Üniversitesi, Türkiye
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale |
| Dergi Adı | Metal Science and Heat Treatment |
| Dergi ISSN | 0026-0673 Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SCI-Expanded |
| Dergi Grubu | Q4 |
| Makale Dili | İngilizce |
| Basım Tarihi | 05-2014 |
| Cilt No | 56 |
| Sayı | 1 |
| Sayfalar | 89 / 92 |
| DOI Numarası | 10.1007/s11041-014-9710-4 |
| Makale Linki | https://link.springer.com/article/10.1007/s11041-014-9710-4 |
| Özet |
| Steel AISI 1050 (steel 50) and chilled cast iron are studied after 5-h solid-phase boronizing from a powder environment at 900°C. The surfaces of the boronized specimens are studied by x-ray and electron microscopic analyses and their Vickers microhardness is measured. The wear resistance is determined by the pin-on-disc method. © 2014 Springer Science + Business Media New York. |
| Anahtar Kelimeler |
| wear | hardness | boronizing | steel | chilled cast iron |